3M DP8625NS
Harmonization Code : 3907.30.00.40 | Epoxy Mold Compounds containing by weight more than 70 % silicon dioxide
Main features
- Flexible Dissimilar Material Bonding
- Controlled Non Sag Dispensing
- Extended Panel Assembly Window
Product Description
3M Scotch-Weld Flexible Acrylic Adhesive DP8625NS is a black, low-odor, non-flammable acrylic structural adhesive supplied in a 10:1 cartridge system for static-mixer dispensing. The non-sag paste holds its shape in vertical joints, panel seams, and gaps between steel, aluminum, composites, and selected plastics. A 21 minute open time provides a defined positioning window, and handling strength develops in approximately 28 minutes at 23 deg C. After seven days, the cured adhesive reaches 200% elongation and Shore D 35 hardness for flexible dissimilar-material assemblies.
Key features
- Flexible Dissimilar Material Bonding: The cured acrylic supports compatible metal, composite, and plastic assemblies.
- Non Sag Cartridge Dispensing: The 10:1 paste formulation controls placement through a static mixer.
- Extended Assembly Window: A 21 minute open time supports positioning before parts are fixed.
Applications
Panel-to-frame bonding, thin-panel assembly, dissimilar-material joining, and controlled gap filling with compatible substrates.
Technical Specifications
No specifications available.
Additional Information
As-supplied / before-processing properties
| Property | Value | Unit | Method / condition |
|---|---|---|---|
| Mix ratio by volume | 10:1 | Base:accelerator | Two-part cartridge system |
| Base color | Black | - | Before mixing |
| Accelerator color | Gray | - | Before mixing |
| Base density | 1.11 | g/cm3 | At 23 deg C |
| Accelerator density | 1.08 | g/cm3 | At 23 deg C |
| Viscosity | Non-sag paste | - | As supplied |
| Open time | 21 | min | Mixed adhesive at 23 deg C |
| Time to handling strength | 28 | min | Mixed adhesive at 23 deg C |
After-processing / final-state properties
| Property | Value | Unit | Method / condition |
|---|---|---|---|
| Color | Black | - | Cured |
| Tensile modulus | 0.7 | MPa | ASTM D638 after 7 days at 23 deg C |
| Tensile stress at break | 1.48 | MPa | ASTM D638 after 7 days at 23 deg C |
| Elongation at break | 200 | % | ASTM D638 after 7 days at 23 deg C |
| Hardness | 35 | Shore D | ASTM D2240 after 7 days at 23 deg C |
| Glass transition temperature | 28 | deg C | Dynamic mechanical analysis after 7 days |